92 Duro Polyurethane Casted

$7.42 – $14.85

SKU: N/A Category:

Available Options:

Description

MATERIAL DESCRIPTION: POLYURETHANE (CREAM, RED, BLUE)
TEMPERATURE RANGE: -30C TO +110C -22F TO + 230F
————————————————————————————————————
PROPERTIES
————————————————————————————————————
HARDNESS- SHORE A 95-96
SHORE D 50-51
25C (77F)
100% MODULUS, PSI (MPA)                                                                      2200 (15.2)
200% MODULUS, PSI (MPA)                                                                     2900 (20.0)
300% MODULUS, PSI (MPA)                                                                     4600 (31.8)
TENSILE, PSI (MPA)                                                                                                       6400 (44.1)
ELONGATION, % 350
D-470 APLIT TEAR, PLI (KN/M)                                                                     140 (24.5)
DIE C TEAR, PLI (KN/M)                                                                                                     650 (111)
BASHORE REBOUND                                                                     44
COMPRESSION SET METHOD B
22 HRS. @ 158F 36
SPECIFIC GRAVITY                                                                                                                                       1.13
100C (212F)
100% MODULUS, PSI (MPA)                                                                                                       1800 (12.4)
200% MODULUS, PSI (MPA)                                                                                                       1900 (13.1)
300% MODULUS, PSI (MPA)                                                                                                       2300 (15.9)
TENSILE, PSI (MPA)                                                                                                                                         4000 (27.6)
ELONGATION, % 410
D-470 SPLIT TEAR, PLI (KN/M)                                                                                                       70 (12.3)
125C (257F)
100% MODULUS, PSI (MPA)                                                                                                       1530 (10.0)
200% MODULUS, PSI (MPA)                                                                                                       1630 (11.3)
300% MODULUS, PSI (MPA)                                                                                                       1960 (13.5)
TENSILE, PSI (MPA)                                                                                                       2400 (16.5)
ELONGATION,                                                                                                       % 340
D-470 SPLIT TEAR, PLI (KN/M)                                                                     55 (9.6)